Technical Documents
PS, Impact Modified.
Details
CAS
9003-55-8
Product Type
Producer
Advantages
- High Gloss
Other Applications
Electric/Electronic Components
Stationary Articles
Food Containers
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Melting range | 190 - 220 | ºC | injection molding |
Humidity | <0.01 | % | injection molding |
MFI | 6 | g/10min | Temperature 200 °C, Load 5 kg, ASTM D1238(G) |
Specific Gravity | 1.05 | ASTM D792 | |
Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | Thickness 3.2 mm, ASTM D955 |
MFI | 69 | g/10min | ASTM D1238(G), Temperature 220 °C, Load 10 kg |
MFI | 16 | g/10min | ASTM D1238 (I), Temperature 230 °C, Load 3.8 kg |
Thermal Properties | |||
Dry Time | 120 - 240 | min | injection molding |
Heat Deflection temperature | 83 | ºC | |
Vicat softening temperature | 95 | ºC | |
UL RTI | 50 | ºC | Thickness 1.5 , 3 mm |
Mechanical Properties | |||
Tensile strength | 34.3 | MPa | Yield, 50 mm/min ; ASTM D638, Thickness 3.2 mm |
Elongation at break-MD | 79 | % | Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
Elongation at yield | 4 | % | Thickness 3.2 mm, 50 mm/min ; ASTM D638 |
Tensile modulus-MD | 2255.5 | MPa | Thickness 3.2 mm, 1 mm/min; ASTM D638 |
Flexural strength | 53.9 | MPa | Yield, Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
Flexural modulus-MD | 2667.4 | MPa | , Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
Rockwell Hardness | 109 | ASTM D 785 | |
Electrical Properties | |||
HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 3 mm |
Arc Resistance | 120 - 180 | s | ASTM D 495 |
Dielectric Strength | 40 | Kv/mm | |
Volume resistance | 1e+014 | ohm-cm | |
Hot Wire Ignition | 7 - 15 | s | Thickness 1.5- mm, HWI |
Hot Wire Ignition | 15 - 30 | s | Thickness 3- mm, HWI |
HAI)High Amp Arc Ignition) | 60 - 120 | arcs | Thickness 1.5 mm |
Process Properties | |||
Mold Temperature | 40 - 70 | ºC | injection molding |
Drying Temperature | 80 | ºC | injection molding |
Middle Barrel Temperature | 180 - 200 | ºC | injection molding |