Injection Molding, PC/ABS, General Purpose, High Impact, Halogen Free Flame retardant
Details
CAS
9003-56-9
Applications
Producer
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Humidity | <4 | % | |
Specific Gravity | 1.18 | ||
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
MFI | 18 | g/10min | 250°C/2.16Kg |
Thermal Properties | |||
Heat Deflection temperature | 94 | ºC | Thickness 6.4 mm |
Flameability | Thickness 0.85- mm | ||
Flameability | Thickness 1- mm | ||
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 0.85- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 0.85- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1- mm |
UL RTI | 60 | ºC | Electrical-Thickness 0.85- mm |
Dry Time | 180 - 240 | min | |
Mechanical Properties | |||
Izod impact strength (notched) | >588 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2549.72 | MPa | Thickness 3.2 mm |
Flexural strength | 93.16 | MPa | Thickness 3.2 mm |
Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 50 | % | Thickness 3.2 mm |
Process Properties | |||
Middle Barrel Temperature | 220 - 275 | ºC | |
Mold Temperature | 60 - 80 | ºC | |
Drying Temperature | 80 - 90 | ºC |