Injection Molding, PC/ABS+GF10%, General Purpose, GF Reinforced
Details Compound
CAS
9003-56-9
Reinforced with
Applications
Industry
Producer
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Humidity | <2 | % | |
Specific Gravity | 1.16 - 1.2 | ||
Linear Mold Shrinkage | 0.003 - 0.004 | cm/cm | Thickness 3.2 mm |
MFI | 4 | g/10min | 250°C/2.16Kg |
Thermal Properties | |||
Dry Time | 180 - 240 | min | |
Heat Deflection temperature | 121 | ºC | |
Mechanical Properties | |||
Izod impact strength (notched) | >98.0 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 4805.25 | MPa | Thickness 3.2 mm |
Flexural strength | 137.29 | MPa | Thickness 3.2 mm |
Tensile strength | 88.25 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 6 | % | |
Process Properties | |||
Middle Barrel Temperature | 235 - 255 | ºC | |
Mold Temperature | 50 - 80 | ºC | |
Drying Temperature | 85 - 95 | ºC |