Details
Product Type
Applications
Producer
Advantages
- High strength
- High gloss
- high impact equivalent to ABS
- Excellent mechanical properties compare with general HIPS
- Meet requirements for cost and quality
Other Applications
big size electric appliances
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
MFI | 6.5 | g/10min | 200°C, 5kg, ASTM D 1238ASTM D 1238 |
Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | ASTM D955 |
Density | 1.04 | g/ml | ASTM D792 |
Thermal Properties | |||
Heat Deflection temperature | 81 | ºC | Thickness 0.5 in, Unannealed; ASTM D648, 1.8MPa |
Vicat softening temperature | 101 | ºC | 1000 g; ASTM D 1525 |
Flameability | 1/16 in | ||
Flameability | 1/8 in | ||
Mechanical Properties | |||
Tensile strength | 26.5 | MPa | at Yield, 50 mm/min ; ASTM D638 |
Elongation at break-MD | 70 | % | 50 mm/min ; ASTM D638 |
Flexural strength | 44.2 | MPa | Yield, 15 mm/min; ASTM D 790 |
Flexural modulus-MD | 2200 | MPa | 15 mm/min; ASTM D 790 |
Izod impact strength (notched) | 176 | J/m | Thickness 0.125, ASTM D256 |
Izod impact strength (notched) | 147 | J/m | Thickness 0.25, ASTM D256 |
Rockwell Hardness | 98 | ASTM D 785 | |
Electrical Properties | |||
Comparative Tracking Index | 400 - 600 | V | UL Rating PLC 1 (400-600 volts) |
Hot Wire Ignition | 15 - 30 | s | HWI, UL Rating PLC 3 (15-30 sec) |
HAI)High Amp Arc Ignition) | 60 - 120 | arcs | HAI, UL Rating PLC 1 (60-120 arcs) |
Arc Resistance | 60 - 120 | s | UL Rating PLC 6 (60-120 sec) |