Acrylonitrile butadiene styrene (ABS) /Polybutylene Terephthalate (PBT) alloy with 15% Glass Fiber. It is suitable for processing through injection molding.
Details Compound
CAS
9003-56-9, 65997-17-3, 24968-12-5 ;25038-59-9
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- Heat Resistance
Other Applications
Electric & Electronic Products (CD ROM Tray)
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| dry Time | 4 - 5 | hr | |
| Physical Properties | |||
| Melting range | 245 - 255 | ºC | |
| Humidity | <0.02 | % | |
| Linear Mold Shrinkage | 0.0040 - 0.0090 | cm/cm | ASTM D955;(Flow), 3.2mm |
| Specific Gravity | 1.33 | ASTM D792 | |
| Thermal Properties | |||
| Flameability | UL94;Thickness >=3.00 mm | ||
| Flameability | UL94;Thickness >=1.50 mm | ||
| UL RTI | 50 | ºC | Thickness >=3.00 mm;Mechanical without Impact |
| UL RTI | 50 | ºC | Thickness >=1.50 mm;Mechanical without Impact |
| UL RTI | 50 | ºC | Thickness >=1.50 mm;Mechanical with Impact |
| UL RTI | 50 | ºC | Thickness >=3.00 mm;Mechanical with Impact |
| UL RTI | 50 | ºC | Thickness >=3.00 mm;Electrical |
| UL RTI | 50 | ºC | Thickness >=1.50 mm;Electrical |
| Heat Deflection temperature | 175 | ºC | ASTM D648;6.4mm;(Unannealed);at 1.8 MPa |
| Melting point | 225 | ºC | Peak at Break |
| Mechanical Properties | |||
| Izod impact strength (notched) | 78.5 | J/m | ASTM D256;23℃;3.2mm |
| Flexural modulus-MD | 4410 | MPa | ASTM D790;1.3mm/min;3.2mm |
| Flexural strength | 127 | MPa | ASTM D790;1.3mm/min;3.2mm;Yield |
| Elongation at break-MD | 3 | % | ASTM D638;5mm/min;3.2mm |
| Tensile Stress at yield-MD | 77.5 | MPa | ASTM D638;5mm/min;3.2mm |
| Electrical Properties | |||
| HAI)High Amp Arc Ignition) | 30 - 60 | arcs | Thickness 1.50 mm |
| HAI)High Amp Arc Ignition) | 30 - 60 | arcs | Thickness 3.00 mm |
| Hot Wire Ignition | 15 - 30 | s | Thickness >=3.00 mm |
| Arc Resistance | 120 - 180 | s | ASTM D495 |
| Hot Wire Ignition | 7 - 15 | s | Thickness >=1.50 mm |
| Dielectric Strength | 21 | Kv/mm | ASTM D149;Thickness 1.00 mm |
| Comparative Tracking Index | 250 | V | Solution A; IEC 60112 |
| Volume resistance | 1.00e+15 | ohm-cm | ASTM D257 |
| Process Properties | |||
| Drying Temperature | 100 | ºC | |
| Mold Temperature | 60 - 90 | ºC | |
| Middle Barrel Temperature | 230 - 245 | ºC | |