myRazalen® P121 TR20 is a general purpose, black colored impact copolymer polypropylene (PP) grade reinforced with 20 % talc.It is suitable for processing by injection molding. Used in automotive interior trim.
Details Compound
Product Type
Reinforced with
Applications
Producer
Chemical Composition
copolymer polypropylene
Advantages
- impact resistance
- good rigidity
- excellent processability
- general purpose
Other Applications
automotive interior trim
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| dry Time | 2 - 4 | hr | |
| Processing Temperature | 220 - 250 | ºC | |
| Appearance Properties | |||
| Physical state | Granulated | ||
| Appearance | Black | ||
| Physical Properties | |||
| Shrinkage | 0.78 | % | ASTM D955; Linear |
| MFI | 20 | g/10min | ASTM D1238;230°C, 2.16 kg |
| Density | 1.06 | g/ml | ASTM D792 |
| Thermal Properties | |||
| Heat Deflection temperature | 110 | ºC | ASTM D648;at 0.46 MPa, Unannealed |
| Heat Deflection temperature | 62 | ºC | ASTM D648;at 1.8 MPa, Unannealed |
| Mechanical Properties | |||
| (Izod impact strength(notched | 6 | kJ/m² | ASTM D256; at 23°C |
| Flexural modulus-MD | 2000 | MPa | ASTM D790 |
| Flexural strength | 26 | MPa | ASTM D790 |
| Elongation at break-MD | 30 | % | ASTM D638 |
| Tensile Stress at yield-MD | 22 | MPa | ASTM D638 |
| Process Properties | |||
| Drying Temperature | 80 - 100 | ºC | |
| Middle Barrel Temperature | 190 - 210 | ºC | |
| Mold Temperature | 30 - 65 | ºC | |
Contact Supplier
To contact the suppliers of this material and register a request for a price, sample, consultation or pre-invoice, please complete the application form.