Razalen® Q121 TR20 is a black colored polypropylene (PP) grade reinforced with 20 % talc. It is suitable for processing by injection molding. Used in various industrial and high performance applications.
Details Compound
Product Type
Reinforced with
Applications
Producer
Chemical Composition
polypropylene (PP)
Advantages
- high stiffness
- good scratch resistance
Other Applications
various industrial and high performance applications
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
dry Time | 2 - 4 | hr | |
Processing Temperature | 220 - 250 | ºC | |
Appearance Properties | |||
Physical state | Granulated | ||
Appearance | Black | ||
Physical Properties | |||
Shrinkage | 1.1 | % | ISO 294-4; Linear |
MFI | 12 | g/10min | ISO 1133;230°C, 2.16 kg |
Density | 1.05 | g/ml | ISO 1182 |
Thermal Properties | |||
Heat Deflection temperature | 67 | ºC | ISO75-2;at 1.8 MPa, Unannealed |
Heat Deflection temperature | 120 | ºC | ISO75-2;at 0.46 MPa, Unannealed |
Mechanical Properties | |||
Izod impact strength (notched) | 35 | J/m | ISO180; at 23°C |
Flexural modulus-MD | 2900 | MPa | ISO178 |
Elongation at break-MD | 30 | % | ISO 527-2 |
Flexural strength | 50 | MPa | ISO178 |
Tensile Stress at yield-MD | 40 | MPa | ISO 527-2 |
Process Properties | |||
Middle Barrel Temperature | 205 - 225 | ºC | |
Drying Temperature | 80 - 100 | ºC | |
Mold Temperature | 50 - 80 | ºC |