Technical Documents
Description: ROHACELL® is produced by thermal expansion of a co-polymer sheet of methacrylic acid and methacrylonitrile. During the foaming process the copolymer sheet is converted to PMI- PolyMethacrylImide. Alcohol is used as a blowing agent,thus ROHACELL® contains no fluorinated carbon hydrates and is halogen free. Information provided by degussa.
Details
Product Type
Producer
Supplier
Advantages
- very homogeneous cell structure
- isotropic properties
- closed-cell rigid foam plastic based on PMI (polymethacrylimide)
- does not contain any CFCs
- Curing temperature up to 130C (266F)
- Curing pressure up to 0.35 MPa (50 psi)
- easy to shape
- Thermoformability
- Sandwich components using ROHACELL® A as core material can be realized in a single work step (=
- cocuring).
- The structural components can be manufactured in an autoclave and by means of RTM.
Other Applications
The field of application for ROHACELL® A is aircraft construction.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 0.110 | g/ml | DIN 53420, ISO 845, ASTM D 1622 |
Thermal Properties | |||
Maximum Service Temperature | 180 | ºC | Heat Distortion Resistance; DIN 53424; Air |
Mechanical Properties | |||
shear modulus | 50 | MPa | DIN 53294, ASTM C 273 |
Elongation at break-MD | 4.5 | % | DIN 53455, ISO 527-2, ASTM D 638 |
Tensile Stress at break-MD | 3.50 | MPa | DIN 53455, ISO 527-2, ASTM D 638 |
shear strength | 2.40 | MPa | DIN 53294, ASTM C 273 |
Tensile modulus-MD | 160 | MPa | ISO 527-2, ASTM D 638 |
Compressive Strength | 3.00 | MPa | DIN 53421, ISO 844, ASTM D 1621 |
Flexural strength | 4.50 | MPa | DIN 53423, ISO 1209, ASTM D 790 |