SIPERNAT® 310 is a very finely ground silica with a very high surface area (BET).
Details
112926-00-8
- Increase in color density and enhanced dot definition are benefits of this product applied as coating pigment for inkjet papers
as an antiblocking agent in polyolefins and PVC
as coating pigment for inkjet papers
as binder or carrier in heterogeneous catalysts
Our silica products are inert and extremely stable chemically. However, due to their high specific surface area, they can absorb moisture and volatile organic compounds from the surrounding atmosphere. Therefore, we recommend recommend storing the products in sealed containers in a dry, cool place, and removed from volatile organic substances. Even if a product is stored under these conditions, after a longer period it can still pick up ambient moisture over time, which could lead to its exceeding the specified moisture content. For this reason, our recommended use-by date is 24 months after date of manufacture. Product more than 24 months old should be tested for moisture content before use in order to make certain that it is still suitable for the intended application.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Sieve residue | <200 | 45μm ;spray; following ISO3262-19 | |
Particle size | 8.5 | µm | d50 Laser diffraction following ISO 13320-1 |
Physical state | powder | ||
Physical Properties | |||
SiO2 | >97 | % | ( ISO 3262-19; based on ignited substance (2 h/1000°C |
Tap density | 0.095 | g/cm3 | not sieved following ISO 787-11 |
pH | 6 | 5%in water; following ISO 787-9 | |
Surface Area | 700 | m²/g | ISO 9277 |
Thermal Properties | |||
Loss on ignition | <6.5 | % | 2h at 1000°C following ISO 3262-1 |
Chemical Properties | |||
Sodium/potassium content | <10000 | ppm | (Na;internal method; based on ignited substance (2 h/1000°C |
Loss on drying | <5 | % | 2h at 105°C following ISO 7872 |
Sulfate content | <1.5 | internal method; based on original substance | |
Electrical Properties | |||
Electrical conductivity | <0.0012 | s/cm | 4%in water; following ISO 787-14 |