starex® BF-0370

Technical Documents

starex® BF-0370 is an eco-friendly, scratch resistant acrylonitrile butadiene styrene (ABS) and polymethyl methacrylate (PMMA) grade .Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Acrylics & Acrylic Copolymers

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • excellent impact strength
  • excellent processability & coloring properties
  • good chemical resistance to especially IPA & ethanol
  • excellent surface gloss
  • scratch resistant
  • eco-friendly
Other Applications

electric products
household appliances/consumer Goods

Technical data

Quantity Value Unit Comment
Appearance Properties
Physical state Pill
Appearance Natural colors
Physical Properties
Shrinkage 0.3 - 0.6 % (ASTM D955;Flow, 3.2 mm (MD
Humidity <0.05 %
MFI 15 g/10min ISO 1133;220℃/10kg
Density 1.06 g/ml ISO 1183
Thermal Properties
Heat Deflection temperature 104 ºC ISO 75-2;0.45 MPa, 4.0 mm, Annealing
Heat Deflection temperature 101 ºC ISO 75-2;1.8 MPa, 4.0 mm, Annealing
Heat Deflection temperature 96 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Dry Time 120 - 240 min
UL RTI 60 ºC Mechanical without Impact, 1.0 mm, 1.5 mm, 3.0 mm
Dry Time 120 - 180 min
UL RTI 60 ºC Mechanical with Impact, 1.0 mm, 1.5 mm, 3.0 mm
UL RTI 60 ºC Electric, 1.0 mm, 1.5 mm, 3.0 mm
Vicat softening temperature 104 ºC ISO R 306;B/120
Vicat softening temperature 102 ºC ISO R 306;B/50
Heat Deflection temperature 84 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Pencil Hardness H JIS K 5401;1000 g
Rockwell Hardness 115 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 16 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 11 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 2700 MPa ISO 178;2mm/min
Flexural strength 90 MPa ISO 178;2mm/min
Tensile Stress at break-MD 48 MPa ISO 527;50mm/min
Strain at break-MD 10 % ISO 527;50mm/min
Tensile Stress at yield-MD 45 MPa ISO 527;50mm/min
Tensile modulus-MD 2400 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >400 ºC