mystarex® BF-0670T is an eco-friendly, scratch resistant acrylonitrile butadiene styrene (ABS) and polymethyl methacrylate (PMMA) grade. .Can be processed using injection molding.
Details
Applications
Industry
Producer
Advantages
- excellent impact strength
- excellent processability & coloring properties
- good chemical resistance to especially IPA & ethanol
- excellent surface gloss
- scratch resistant
- eco-friendly
Other Applications
electric products
household appliances/consumer Goods
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Shrinkage | 0.4 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
| Shrinkage | 0.4 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 24 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.12 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Glow WireTest | 550 | ºC | Glow Wire Ignition Temperature;IEC 60695-2-13;2.0 mm |
| Glow WireTest | 550 | ºC | Glow Wire Flammability Index;IEC 60695-2-12;2.0 mm |
| Dry Time | 120 - 240 | min | |
| Dry Time | 120 - 180 | min | |
| UL RTI | 50 | ºC | Mechanical without Impact, 0.8 mm, 2.0 mm, 3.0 mm |
| UL RTI | 50 | ºC | Mechanical with Impact, 0.8 mm, 2.0 mm, 3.0 mm |
| UL RTI | 50 | ºC | Electric, 0.8 mm, 2.0 mm, 3.0 mm |
| Vicat softening temperature | 92 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 90 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 92 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 86 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 83 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 72 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Pencil Hardness | H | JIS K 5401;1000 g | |
| Rockwell Hardness | 115 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 7.4 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2360 | MPa | ISO 178;2mm/min |
| Flexural strength | 70 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 36 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2500 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 22 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 52 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |