starex® EG-7000

Technical Documents

starex® EG-7000 is an eco-friendly, post-consumer materials (PCM)-based acrylonitrile butadiene styrene (ABS) and polyethylene terephthalate (PET) grade.Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polyesters

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • helps in reduction of carbon emission
  • good chemical resistance
  • well balanced properties
  • eco-friendly
Other Applications

Automotive
Electronics / Computers > Monitors, OA machines
Telecom > Cellular phones

Handling

It complies with the EPEAT Gold & TCO Edge eco-certifications, and RoHS regulation.

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Shrinkage 0.46 - 0.57 % (ISO 2577;Cross flow, 3.2 mm (TD
Shrinkage 0.44 - 0.54 % (ISO 2577;Flow, 3.2 mm (MD
Humidity <0.05 %
MFI 35 g/10min ISO 1133;250℃/10kg
Density 1.08 g/ml ISO 1183
Thermal Properties
Auto-ignition temperature >400 ºC
Dry Time 120 - 240 min
Dry Time 120 - 180 min
UL RTI 60 ºC Mechanical without Impact, 1.5 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 1.5 mm, 3.0 mm
UL RTI 60 ºC Electric, 1.5 mm, 3.0 mm
Vicat softening temperature 91 ºC ISO R 306;B/120
Vicat softening temperature 90 ºC ISO R 306;B/50
Heat Deflection temperature 97 ºC ISO 75-2;0.45 MPa, 4.0 mm, Annealing
Heat Deflection temperature 88 ºC ISO 75-2;1.8 MPa, 4.0 mm, Annealing
Heat Deflection temperature 78 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Heat Deflection temperature 78 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 95 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 20 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 21 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 1960 MPa ISO 178;2mm/min
Flexural strength 55 MPa ISO 178;2mm/min
Tensile Stress at break-MD 26 MPa ISO 527;50mm/min
Tensile modulus-MD 2000 MPa ISO 527;50mm/min
Strain at break-MD 18 % ISO 527;50mm/min
Tensile Stress at yield-MD 38 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >300 ºC
Optical Properties
Yellow index 20 ASTM D1925;3.2 mm