Technical Documents
starex® QU-0191 S is an acrylonitrile butadiene styrene (ABS) grade. Can be processed using extrusion.
Details
Product Type
Applications
Producer
Advantages
- good sheet extrusion stability
- good chemical- & crack resistance
- good vacuum moldability
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
Other Applications
Appliances > Refrigerators
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
MFI | 4.3 | g/10min | ISO 1133;220℃/10kg |
Density | 1.04 | g/ml | ISO 1183 |
Shrinkage | 0.4 - 0.6 | % | (ASTM D955;Flow, 3.2 mm (MD |
Thermal Properties | |||
Dry Time | 120 - 180 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 0.75 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 0.75 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 0.75 mm, 3.0 mm |
Vicat softening temperature | 102 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 103 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 100 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 94 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 81 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Charpy Impact Strength (notched) | 26 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 26 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2500 | MPa | ISO 178;2mm/min |
Flexural strength | 70 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 40 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2500 | MPa | ISO 527;50mm/min |
Strain at break-MD | 14 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 39 | MPa | ISO 527;50mm/min |
Rockwell Hardness | 108 | ISO 2039-2;R Scale | |
Chemical Properties | |||
Decomposition temperature | >400 | ºC |