mystarex® QU-0191 SV is an acrylonitrile butadiene styrene (ABS) grade. Can be processed using injection molding.
Details
Product Type
Applications
Producer
Advantages
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
- good moldability
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Humidity | <0.05 | % | |
| MFI | 4.3 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.04 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Dry Time | 120 - 180 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 0.75 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 0.75 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 0.75 mm, 3.0 mm |
| Vicat softening temperature | 104 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 102 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 95 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 83 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 112 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 25 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 25 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2700 | MPa | ISO 178;2mm/min |
| Flexural strength | 82 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 41 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2600 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 12 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 54 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |