mystarex® SF-0941 is an eco-friendly, scratch resistant acrylonitrile butadiene styrene (ABS) and polymethyl methacrylate (PMMA) grade. Can be processed using injection molding.
Details
Applications
Industry
Producer
Advantages
- excellent impact strength
- excellent processability & coloring properties
- good chemical resistance to especially IPA & ethanol
- excellent surface gloss
- scratch resistant
- eco-friendly
Other Applications
Electronics / Computers > TV housings, monitor and home theater
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Shrinkage | 0.5 - 0.7 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 26 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.16 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Dry Time | 120 - 180 | min | |
| Vicat softening temperature | 105 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 102 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 92 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 80 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 116 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 7.9 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 6.9 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2500 | MPa | ISO 178;2mm/min |
| Flexural strength | 89 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 51 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2700 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 15 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 64 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |