starex® SH-0160 is an acrylonitrile butadiene styrene (ABS) grade. Can be processed using extrusion.
Details
Product Type
Applications
Producer
Advantages
- good sheet extrusion stability
- good chemical- & crack resistance
- good vacuum moldability
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
Other Applications
Buildings & constructions
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| MFI | 8 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.04 | g/ml | ISO 1183 |
| Shrinkage | 0.4 - 0.6 | % | (ASTM D955;Flow, 3.2 mm (MD |
| Thermal Properties | |||
| Dry Time | 120 - 180 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
| Vicat softening temperature | 99 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 90 | ºC | ASTM D648;18.56 kgf/cm2, 6.4 mm |
| Mechanical Properties | |||
| Rockwell Hardness | 101 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 27 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| Flexural modulus-MD | 1800 | MPa | ISO 178;5mm/min |
| Flexural strength | 55 | MPa | ISO 178;5mm/min |
| Strain at break-MD | 80 | % | ASTM D638;5mm/min |
| Tensile Stress at yield-MD | 35 | MPa | ISO 527;50mm/min |
| Izod impact strength (notched) | 323.6 | J/m | ASTM D256;1/4 inch, 23°C |
| Izod impact strength (notched) | 441.3 | J/m | ASTM D256;1/8 inch, 23°C |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |