starex® SP-0170 is an acrylonitrile butadiene styrene (ABS) grade. Can be processed using extrusion.
Details
Product Type
Applications
Producer
Advantages
- good sheet extrusion stability
- good chemical- & crack resistance
- good vacuum moldability
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
Other Applications
Pipes, Hoses & Fittings
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Physical state | Pill | ||
Appearance | Natural colors | ||
Physical Properties | |||
MFI | 6.4 | g/10min | ISO 1133;220℃/10kg |
Density | 1.04 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 103 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 99 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 93 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 81 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Vicat softening temperature | 99 | ºC | ISO R 306;B/50 |
Dry Time | 120 - 180 | min | |
Mechanical Properties | |||
Charpy Impact Strength (notched) | 34 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 34 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 1900 | MPa | ISO 178;2mm/min |
Flexural strength | 60 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 31 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 1900 | MPa | ISO 527;50mm/min |
Strain at break-MD | 19 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 40 | MPa | ISO 527;50mm/min |
Rockwell Hardness | 101 | ISO 2039-2;R Scale | |
Chemical Properties | |||
Decomposition temperature | >400 | ºC |