mystarex® SP-0180 D is an acrylonitrile butadiene styrene (ABS) grade.Can be processed using injection molding.
Details
Product Type
Applications
Producer
Advantages
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
- good moldability
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Humidity | <0.005 | % | |
| MFI | 4.5 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.04 | g/ml | ISO 1183 |
| Shrinkage | 0.4 - 0.6 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Thermal Properties | |||
| Dry Time | 120 - 180 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 0.75 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 0.75 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 0.75 mm, 3.0 mm |
| Vicat softening temperature | 102 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 96 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 81 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 101 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 38 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 40 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 1600 | MPa | ISO 178;2mm/min |
| Flexural strength | 58 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 35 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2100 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 13 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 41 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |