mystarex® SP-0180 is an acrylonitrile butadiene styrene (ABS) grade. Can be processed using extrusion.
Details
Product Type
Applications
Producer
Advantages
- good sheet extrusion stability
- good chemical- & crack resistance
- good vacuum moldability
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
Other Applications
Pipes, Hoses & Fittings
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Physical state | Pill | ||
| Appearance | Natural colors | ||
| Physical Properties | |||
| MFI | 6 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.04 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Vicat softening temperature | 97 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 104 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 100 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 92 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 77 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Vicat softening temperature | 99 | ºC | ISO R 306;B/120 |
| Dry Time | 120 - 180 | min | |
| Mechanical Properties | |||
| Charpy Impact Strength (notched) | 38 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 36 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2100 | MPa | ISO 178;2mm/min |
| Flexural strength | 65 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 32 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2000 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 13 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 45 | MPa | ISO 527;50mm/min |
| Rockwell Hardness | 101 | ISO 2039-2;R Scale | |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |