starex® SV-0157 V is an acrylonitrile butadiene styrene (ABS) grade.Can be processed using injection molding.
Details
Product Type
Applications
Producer
Advantages
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
- good moldability
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Shrinkage | 0.5 - 0.6 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
Shrinkage | 0.5 - 0.6 | % | (ISO 2577;Flow, 3.2 mm (MD |
Humidity | <0.02 | % | |
MFI | 5 | g/10min | ISO 1133;220℃/10kg |
Density | 1.06 | g/ml | ISO 1183 |
Thermal Properties | |||
Dry Time | 120 - 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm, 6.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm, 6.0 mm |
UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm, 6.0 mm |
Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 90 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 80 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 108 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 30 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 30 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2400 | MPa | ISO 178;2mm/min |
Flexural strength | 65 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 35 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2300 | MPa | ISO 527;50mm/min |
Strain at break-MD | 10 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 45 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC | |
Electrical Properties | |||
HAI)High Amp Arc Ignition) | arcs | 1.5mm, 3.0 mm, 6.0 mm | |
Hot Wire Ignition | 2 | s | 6.0mm |
Hot Wire Ignition | 4 | s | 1.5mm |
Hot Wire Ignition | 3 | s | 3.0mm |