starex® SV-0167 V is an acrylonitrile butadiene styrene (ABS) grade. Can be processed using injection molding.
Details
Product Type
Applications
Producer
Advantages
- high impact & modulus characteristics
- excellent colorability & gloss
- good tensile strength and rigidity
- good heat resistance
- good moldability
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Physical Properties | |||
| Shrinkage | 0.5 - 0.6 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 5.2 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.03 | g/ml | ISO 1183 |
| Shrinkage | 0.5 - 0.6 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
| Thermal Properties | |||
| Dry Time | 120 - 180 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
| Vicat softening temperature | 98 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 92 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 78 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Mechanical Properties | |||
| Rockwell Hardness | 100 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 35 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 33 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2000 | MPa | ISO 178;2mm/min |
| Flexural strength | 65 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 35 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2000 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 15 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 40 | MPa | ISO 527;50mm/min |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |