starex® TX-0510

Technical Documents

starex® TX-0510 is a transparent acrylonitrile butadiene styrene (ABS) grade. Can be processed using injection molding.

Details

Product Type

Polymer > ABS

Applications

Polymers industry > Injection moulding

Industry

Electronics
Food industry

Producer

Samsung

Advantages
  • excellent balance of transparency, mechanical properties, & processability
  • excellent color consistency & stability
Other Applications

Households products/ Consumer Goods > Toys
Packaging >food containers
Electronics / Computers > TV housings
Appliances > dust box of vacuum cleaner
Appliances > washing machine top cover

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance
Physical state Pill
Physical Properties
Shrinkage 0.44 - 0.54 % (ISO 2577;Cross flow, 3.2 mm (TD
Shrinkage 0.43 - 0.52 % (ISO 2577;Flow, 3.2 mm (MD
Humidity <0.05 %
Density 1.1 g/ml ISO 1183
MFI 16 g/10min ISO 1133;220℃/10kg
Thermal Properties
Dry Time 120 min
UL RTI 50 ºC Mechanical without Impact, 1.5 mm, 3.0 mm
Vicat softening temperature 88 ºC ISO R 306;B/50
UL RTI 50 ºC Electric, 1.5 mm, 3.0 mm
UL RTI 50 ºC Mechanical with Impact, 1.5 mm, 3.0 mm
Heat Deflection temperature 78 ºC ASTM D648;18.56 kgf/cm2, 6.4 mm
Mechanical Properties
Rockwell Hardness 110 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 13 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 12 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 2200 MPa ISO 178;2mm/min
Flexural strength 70 MPa ISO 178;2mm/min
Tensile Stress at yield-MD 47 MPa ISO 527;50mm/min
Strain at break-MD 19 % ISO 527;50mm/min
Tensile modulus-MD 1981 MPa ISO 527;50mm/min
Tensile Stress at break-MD 32.36 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >400 ºC