ststarex® TX-0520I is a transparent acrylonitrile butadiene styrene (ABS) grade. Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- excellent balance of transparency, mechanical properties, & processability
- excellent color consistency & stability
Other Applications
Households products/ Consumer Goods > Toys
Packaging >food containers
Electronics / Computers > TV housings
Appliances > dust box of vacuum cleaner
Appliances > washing machine top cover
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | |||
Physical state | Pill | ||
Physical Properties | |||
Shrinkage | 0.6 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
Shrinkage | 0.4 | % | (ISO 2577;Flow, 3.2 mm (MD |
Humidity | <0.05 | % | |
MFI | 18 | g/10min | ISO 1133;220℃/10kg |
Density | 1.09 | g/ml | ISO 1183 |
Thermal Properties | |||
Vicat softening temperature | 91 | ºC | ISO R 306;B/50 |
Dry Time | 240 | min | |
UL RTI | 50 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
UL RTI | 50 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
UL RTI | 50 | ºC | Electric, 1.5 mm, 3.0 mm |
Heat Deflection temperature | 82 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 71 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 108 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 12 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2200 | MPa | ISO 178;2mm/min |
Flexural strength | 70 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 40 | MPa | ISO 527;5mm/min |
Tensile modulus-MD | 1900 | MPa | ISO 527;5mm/min |
Strain at break-MD | 20 | % | ISO 527;5mm/min |
Tensile Stress at yield-MD | 47 | MPa | ISO 527;5mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC | |
Optical Properties | |||
Haze | 2 | % | ISO 13468;3.2 mm |
Transmittance | 90 | % | ISO 13468;3.2 mm |