Technical Documents
starex® VG-4920F is a flame retardant acrylonitrile butadiene styrene (ABS) grade reinforced with 20 % glass fiber.Can be processed using injection molding.
Details Compound
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- excellent flexural modulus
- excellent heat resistance
- excellent dimensional stability
- high impact strength
- less changes in mechanical property over a wide temperature range
Other Applications
Appliances > Air conditioning
Automotive>interior
Electronics / Computers > television, monitor, OA machine
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Flame Rating | IEC 60695-11-10, IEC 60695-11-20;2.0 mm, 3.0 mm, ALL | ||
Flame Rating | IEC 60695-11-10, IEC 60695-11-20;1.6 mm, ALL | ||
Processing Temperature | 180 - 190 | ºC | |
Processing Temperature | 200 - 210 | ºC | |
Processing Temperature | 220 - 230 | ºC | |
dry Time | 2 - 3 | hr | |
Ash content | 20 | % | ISO 3451 |
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Humidity | <0.05 | % | |
MFI | 41 | g/10min | ISO 1133;220℃/10kg |
Density | 1.34 | g/ml | ISO 1183 |
Shrinkage | 0.1 - 0.3 | % | (ASTM D955;Flow, 3.2 mm (MD |
Thermal Properties | |||
UL RTI | 60 | ºC | Mechanical without Impact, 1.6 mm, 2.0 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.6 mm, 2.0 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.6 mm, 2.0 mm, 3.0 mm |
Heat Deflection temperature | 100 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 95 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Vicat softening temperature | 102 | ºC | ISO R 306;B/50 |
Vicat softening temperature | 104 | ºC | ISO R 306;B/120 |
Mechanical Properties | |||
Rockwell Hardness | 116 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 9.1 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 9.1 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 7100 | MPa | ISO 178;2mm/min |
Flexural strength | 146 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 101 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 6100 | MPa | ISO 527;50mm/min |
Strain at break-MD | 2.4 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 102 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC | |
Electrical Properties | |||
Hot Wire Ignition | 2 | s | 3.0mm |
Hot Wire Ignition | 3 | s | 1.6mm |
HAI)High Amp Arc Ignition) | arcs | 1.6mm, 3.0 mm | |
Comparative Tracking Index | 3 | V | |
Process Properties | |||
Mold Temperature | 40 - 80 | ºC | |
Drying Temperature | 80 | ºC |