myPermanently transparent polymer blend of amorphous (PA6-3-T) and partially crystalline Polyamide
Details
Product Type
Applications
Industry
Producer
Supplier
Advantages
- stress crack resistant
- low water absorption
- very good flow properties
- UV and weathering stabilized
Other Applications
Eyeglasses frames, optics industry, medical devices, machinery and equipment parts
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Transparent | ||
| Physical Properties | |||
| Density | 1.12 | g/ml | |
| Linear Mold Shrinkage | cm/cm | Transverse | |
| Linear Mold Shrinkage | cm/cm | Flow | |
| Thermal Properties | |||
| Heat Deflection temperature | 93 | ºC | 1.8 MPa |
| Glass transition Temperature | 108 | ºC | |
| Flameability | Thickness 1.6 mm | ||
| Heat Deflection temperature | 100 | ºC | 0.46 MPa |
| Thermal Expansion | <50 | µm/m-°C | 20 °C |
| Vicat softening temperature | 105 | ºC | |
| Flameability | Thickness 3.2 mm | ||
| Mechanical Properties | |||
| Tensile modulus-MD | 2800 | MPa | |
| Elongation at break-MD | >50 | % | |
| Tensile strength | 98 | MPa | |
| Elongation at yield | 6 | % | |
| Charpy Impact Strength (notched) | 0.6 | kJ/m² | mperature -30 °C |
| Charpy Impact Strength (notched) | 0.9 | kJ/m² | |
| Chemical Properties | |||
| Water absorption | 9 | % | |
| Electrical Properties | |||
| Dissipation Factor | 0.03 | ||
| Dielectric Constant | 3 | 1000000 Hz | |
| Comparative Tracking Index | 600 | V | |
| Surface Resistance | >1.000E+015 | ohm | |
| Dielectric Strength | 21 | Kv/mm | |
| Electrical Resistivity | >1.000E+015 | ohm-cm | |