myVESTAKEEP® 2000 FC30 is a semi-crystalline, medium viscosity, self-extinguishing polyether ether ketone (PEEK) resin reinforced with carbon fiber, graphite and PTFE (10:10:10). It can be processed by injection molding. Suitable for automotive applications such as bearings, bushings and gearbox parts. Complies with FDA, UL flammability and EU (10/2011) regulations.
Details Compound
Product Type
Reinforced with
Producer
Supplier
Advantages
- excellent mechanical-, thermal-, hydrolysis-, wear- and chemical resistance
- good physical stability
- dimensional stability
- processability
- non-combustible & recyclable
- self-lubricating nature
Other Applications
automotive applications such as bearings, bushings and gearbox parts
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Physical state | Pill shape | ||
| Physical Properties | |||
| MFI | 21.75 | g/10min | 380°C/5 kg- ISO 1133 |
| Density | 1.45 | g/ml | ISO 1183- 23°C |
| Shrinkage | 0.1 | % | ISO 294-4, 2 mm, Flow |
| Shrinkage | 0.4 | % | ISO 294-4, 2 mm, Transverse |
| Melting range | 370 - 380 | ºC | |
| Thermal Properties | |||
| Melting point | 340 | ºC | ISO 11357, DSC - 2nd heating |
| Vicat softening temperature | 335 | ºC | ISO 306, 50N, Method B |
| Heat Deflection temperature | 337 | ºC | ISO 75-1, 0.45 MPa, Method B |
| Heat Deflection temperature | 320 | ºC | ISO 75-1, 1.8 MPa, Method A |
| Vicat softening temperature | 340 | ºC | ISO 306, 10N, Method A |
| Flameability | UL 94, 1.6 mm | ||
| Glass transition Temperature | 150 | ºC | |
| Dry Time | 240 | min | |
| Mechanical Properties | |||
| (Charpy Impact Strength(unnotched | 40 | kJ/m² | ISO 179/1eU, 23°C, Complete break |
| Strain at break-MD | 2 | % | ISO 527-2 |
| Tensile strength | 145 | MPa | ISO 527-1 |
| Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA, 23°C, Complete break |
| Tensile modulus-MD | 23000 | MPa | |
| Charpy Impact Strength (notched) | 5 | kJ/m² | ISO 179/1eA, -30°C, Complete break |
| (Charpy Impact Strength(unnotched | 40 | kJ/m² | ISO 179/1eU, -30°C, Complete break |
| Chemical Properties | |||
| Water absorption | 0.4 | % | ISO 62, 23°C |
| LOI | 47 | % | ISO 4589 |
| Electrical Properties | |||
| Volume resistance | ohm-cm | IEC 60093 | |
| Surface Resistance | ohm | IEC 60093 | |
| Dissipation Factor | 0.02 | %, IEC 60250, 1 MHz | |
| Relative permittivity | 6.1 | IEC 60250, 50 Hz | |
| Relative permittivity | 4.9 | IEC 60250, 1 MHz | |
| Process Properties | |||
| Mold Temperature | 160 - 200 | ºC | |
| Die Temperature | 380 | ºC | |
| Drying Temperature | 160 | ºC | |