myVESTAKEEP® 2000 GF30 is a medium viscosity, self-extinguishing polyether ether ketone (PEEK) resin reinforced with 30% glass fiber. It can be processed by injection molding. Suitable for machinery & apparatus construction, aircraft and electrical industry. Complies with FDA, UL flammability and EU (10/2011) regulations.
Details Compound
Product Type
Reinforced with
Industry
Producer
Supplier
Advantages
- excellent mechanical-, thermal-, hydrolysis-, wear- & chemical resistance
- good electrical properties
- good physical stability
- dimensional stability
- degassing
- fire & ion extraction properties
- processability
- non-combustible
- recyclable
- releases toxic fumes
- self-lubricating nature
Other Applications
machinery & apparatus construction, aircraft and electrical industry
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Physical state | Tablets or cylindrical | ||
| Physical Properties | |||
| Density | 1.5 | g/ml | ISO 1183- 23°C |
| MFI | 25.5 | g/10min | 380°C/5 kg- ISO 1133 |
| Shrinkage | 0.2 | % | ISO 294-4, 2 mm, Flow |
| Shrinkage | 0.7 | % | ISO 294-4, 2 mm, Transverse |
| Melting range | 380 - 400 | ºC | |
| Thermal Properties | |||
| Vicat softening temperature | 335 | ºC | ISO 306, 50N, Method B |
| Melting point | 340 | ºC | ISO 11357, DSC - 2nd heating |
| Heat Deflection temperature | 338 | ºC | ISO 75-1, 0.45 MPa, Method B |
| Vicat softening temperature | 340 | ºC | ISO 306, 10N, Method A |
| Heat Deflection temperature | 323 | ºC | ISO 75-1, 1.8 MPa, Method A |
| Glass transition Temperature | 151 | ºC | |
| Flameability | UL 94, 3.2 mm | ||
| Dry Time | 240 | min | |
| Mechanical Properties | |||
| Tensile strength | 165 | MPa | ISO 527-1 |
| Strain at break-MD | 2 | % | ISO 527-2 |
| (Charpy Impact Strength(unnotched | 55 | kJ/m² | ISO 179/1eU, 23°C, Complete Break |
| Charpy Impact Strength (notched) | 9 | kJ/m² | ISO 179/1eA, 23°C, Complete break |
| Tensile modulus-MD | 11000 | MPa | |
| Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA, |
| (Charpy Impact Strength(unnotched | 65 | kJ/m² | ISO 179/1eU, -30°C, Complete Break |
| Chemical Properties | |||
| LOI | 45 | % | ISO 4589, 3.2 mm |
| Water absorption | 0.4 | % | |
| Electrical Properties | |||
| Surface Resistance | ohm | IEC 60093 | |
| Volume resistance | ohm-cm | IEC 60093 | |
| Dissipation Factor | 0.004 | %, IEC 60250, 1 MHz | |
| Dielectric Strength | 16 | Kv/mm | IEC 60243-1, K20/P50 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Relative permittivity | 3.4 | IEC 60250, 50 Hz | |
| Relative permittivity | 3.3 | IEC 60250, 1 MHz | |
| Process Properties | |||
| Mold Temperature | 160 - 200 | ºC | |
| Die Temperature | 380 | ºC | |
| Drying Temperature | 160 | ºC | |