VESTAKEEP® 2000FP is an unreinforced, medium viscosity, self-extinguishing, semi-crystalline polyether ether ketone (PEEK) powder. Suitable for the manufacture of compression molded parts. Complies with FDA, UL flammability and EU (10/2011) regulations.
Details
Product Type
Applications
Producer
Supplier
Advantages
- excellent thermal- and chemical resistance
- self-extinguishing
Other Applications
the manufacture of compression molded parts
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Particle size | 50 | µm | Malvern Mastersizer |
Physical state | powder | ||
Physical Properties | |||
MFI | 91 | g/10min | 380°C/5 kg- ISO 1133 |
Density | 1.30 | g/ml | ISO 1183- 23°C |
Bulk density | 0.28 | g/ml | ISO 60 |
Thermal Properties | |||
Flameability | UL 94, 1.6 mm | ||
Vicat softening temperature | 335 | ºC | ISO 306, 10N, Method A |
Heat Deflection temperature | 205 | ºC | ISO 75-1, 0.45 MPa, Method B |
Heat Deflection temperature | 155 | ºC | ISO 75-1, 1.8 MPa, Method A |
Vicat softening temperature | 310 | ºC | ISO 306, 50N, Method B |
Melting point | 340 | ºC | ISO 11357, DSC-2nd heating |
Dry Time | 180 | min | |
Mechanical Properties | |||
Tensile modulus-MD | 3700000 | MPa | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU, -30°C | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU, 23°C | |
Tensile Stress at yield-MD | 100 | MPa | ISO 527-1 |
Strain at break-MD | 30 | % | ISO 527-2 |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA, 23°C, Complete break |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA, -30°C, Complete break |
Process Properties | |||
Drying Temperature | 150 | ºC |