Technical Documents
VESTAKEEP® i2 G is a natural colored, standard viscosity polyether ether ketone (PEEK) that is especially designed for long term implantable medical devices. This grade is often used for injection molding processing technologies due to its good flowability.
Details
Product Type
Industry
Producer
Supplier
Advantages
- The extra high purity
- extended quality
- biocompatibility
- permanent tissue/bone contact
- injection molding processing technologies due to its good flowability
Other Applications
permanent implants
Handling
VESTAKEEP® i2 G has been tested following ISO 10993-1.
complies ASTM F2026 “Standard Specification for Polyetheretherketone (PEEK) Polymers for Surgical Implant Applications”.
is supplied as cylindrical pellets.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.30 | g/ml | ISO 1183@ Temperature 23°C |
MVR | 70 | ml/10min | ISO 1133 @Load 5.0 kg,Temperature 380 °C |
Thermal Properties | |||
Heat Deflection temperature | 150 | ºC | ISO 75-1/2;at 1.8 MPa |
Heat Deflection temperature | 205 | ºC | ISO 75-1/2;at 0.45 MPa |
Melting point | 340 | ºC | ISO 11357; DSC; 2nd heating |
Vicat softening temperature | 310 | ºC | 50N; ISO 306 |
Vicat softening temperature | 335 | ºC | 10N; ISO 306 |
Mechanical Properties | |||
Tensile Stress at yield-MD | 100 | MPa | 23°C/ 50% r.h.;ISO 527-1/2 |
Strain at break-MD | >20 | % | 23°C/ 50% r.h.;ISO 527-1/2 |
Elongation at yield | 5.0 | % | 23°C/ 50% r.h.;ISO 527-1/2 |
Tensile modulus-MD | 3700 | MPa | ISO 527-1/2 |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@ Temperature -30°C |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU @ Temperature 23°C ; 50% r.h. | |
Tensile Stress at break-MD | >70 | MPa | 23°C/ 50% r.h.;ISO 527-1/2 |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@ Temperature 23°C ; 50% r.h. |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU @ Temperature -30°C | |
Chemical Properties | |||
Moisture absorption | 0.12 | % | ISO 62@ Temperature 23°C ; 50% r.h. |
Water absorption | 0.4 | % | ISO 62;at saturation |