VESTAKEEP® Ultimate is a semi-crystalline, unreinforced polyether ether ketone grade. Possesses high viscosity. Processed by injection molding and extrusion.
Details
Product Type
Applications
Industry
Producer
Supplier
Advantages
- low ion content
- high melt elasticity
- superior thermal, abrasion and chemical resistance
- high elasticity
- self-extinguishing
- high impact resistance
- good processability
- resilient
Other Applications
automobile and aircraft industries for sensors or ball bearings
as a sealant in oil & gas industry
manufacture of pipes with large diameters
Electronics / Computers
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Physical state | Granulated | ||
Physical Properties | |||
Shrinkage | 0.9 | % | ISO 294-4, in flow direction |
Density | 1.3 | g/ml | ISO 1183- 23°C |
Shrinkage | 1.1 | % | ISO 294-4, in transverse direction |
MFI | 9.1 | g/10min | 380°C/5 kg- ISO 1133 |
Melting range | 370 - 380 | ºC | |
Thermal Properties | |||
Vicat softening temperature | 305 | ºC | ISO 306, 50N, Method A |
Vicat softening temperature | 335 | ºC | ISO 306, 10N, Method A |
Melting point | 340 | ºC | ISO 11357, DSC, 2nd heating |
Flameability | UL94, 3.2 mm | ||
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | 9 | kJ/m² | ISO 179/1eA, 23°C |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU, 23°C | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU, -30°C | |
Tensile Stress at yield-MD | 95 | MPa | ISO 527-1 |
Strain at break-MD | 40 | % | ISO 527-2 |
Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA, -30°C |
Tensile modulus-MD | 3400 | MPa | ISO 527-1 |
Electrical Properties | |||
Comparative Tracking Index | 175 | V | IEC 60112 |
Volume resistance | ohm-cm | IEC 60093 | |
Surface Resistance | ohm | IEC 60093 | |
Comparative Tracking Index | 200 | V | IEC 60112 |
Dielectric Strength | 16 | Kv/mm | IEC 60243-1, K20/P50 |
Relative permittivity | 2.8 | IEC 60250, 1 MHz | |
Process Properties | |||
Mold Temperature | 180 | ºC |