Technical Documents
PA 12 elastomers . Applications: decorative and protective films for sports articles and interior/exterior designs on automobilesInformation provided by degussa.
Details
Product Type
Applications
Producer
Supplier
Chemical Composition
thermoplastic elastomers
Advantages
- low density
- highly resistant to chemicals and solvents
- easy to process and color and are easy to overmold
- can be decorated easily by means of heat transfer printing
- excellent impact strength at low temperatures
- Their hardness and flexibility can be varied over a wide range.
- high elasticity and good recovery
- Their mechanical properties are only slightly temperature-dependent.
- They are free of volatile or migrating plasticizers.
Other Applications
decorative and protective films for sports articles and interior/exterior designs on automobilesInformation provided by degussa.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.01 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 45 | ºC | ISO 75-1; at 1.8 MPa |
Heat Deflection temperature | 100 | ºC | ISO 75-2; at 0.46 MPa |
Vicat softening temperature | 170 | ºC | 10N; ISO 306 |
Thermal Expansion | 160 | µm/m-°C | ISO 11359-2 @Temperature 23.0 -55.0 °C; Transverse |
Thermal Expansion | 50 | µm/m-°C | Transverse to Flow@Temperature 23.0 -55.0 °C |
Thermal Expansion | 160 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0 -55.0 °C; |
Flameability | IEC 60695@1.6 mm | ||
Vicat softening temperature | 130 | ºC | 50N; ISO 306 |
Mechanical Properties | |||
Tensile strength | 27 | MPa | 50%Modulus (Tensile stress at 50%elongation);ISO 527-1, ISO 527-2 |
Hardness Shore D | 68 | ISO 868 | |
Tensile strength | 27 | MPa | at 50% Strain;ISO 527-2 |
Elongation at yield | 19 | % | ISO 527-1, ISO 527-2 |
viscosity number | 190 | ml/g | ISO 307 |
Charpy Impact Strength (notched) | 33 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C ;Partial Break |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
Tensile modulus-MD | 700 | MPa | ISO 527-1, ISO 527-2 |
Elongation at break-MD | >200 | % | ISO 527-1, ISO 527-2 |
Tensile Stress at yield-MD | 31 | MPa | ISO 527-1, ISO 527-2 |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Chemical Properties | |||
Water absorption | 1.5 | % | ISO 62; at Saturation |
Electrical Properties | |||
Comparative Tracking Index | 600 | V | Test Solution A; IEC 60112 |
Surface Resistance | 1.00e+13 | ohm | Spec.; IEC 60093 |
Dissipation Factor | 0.15 | IEC 60250 @100 Hz | |
Dielectric Constant | 7.4 | IEC 60250 @100 Hz | |
Dielectric Constant | 4.6 | IEC 60250 @ 1e+6 Hz | |
Dielectric Strength | 30.0 | Kv/mm | K20/P50; IEC 60243-1 |
Volume resistance | 1.00e+11 | ohm-cm | Spec.; IEC 60093 |
Dissipation Factor | 0.076 | IEC 60250 @ 1e+6 Hz |