VESTAMID® EX9350 is a flexible PEBA (polyether block amide) grade, free from volatile or leaching plasticizers. It can be processed by extrusion. Suitable for brake booster lines in automotive industry.
Details Compound
Product Type
Producer
Supplier
Advantages
- Chemical resistance Good
- Density Low
- Elasticity High
- Flexibility Good
- Impact Resistance Low Temp
- Resilient
- Solvent Resistant
Other Applications
Automotive > Under the hood - Flexible tubes
Conversion of plastisol > Screen printing
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Processing Temperature | 210 - 240 | ºC | |
Appearance Properties | |||
Physical state | Solid | ||
Physical Properties | |||
Shrinkage | 1.1 | % | ISO 294-4,2577; parallel |
Density | 1.05 | g/ml | ISO 1183 |
Shrinkage | 1.0 | % | ISO 294-4,2577; normal |
Thermal Properties | |||
Vicat softening temperature | 130 | ºC | 50°C/hr/50 N; ISO 306 |
Dry Time | 480 - 960 | min | |
Melting point | 198 | ºC | 10°C/min; ISO 11357-1/-3 |
Heat Deflection temperature | 130 | ºC | ISO 75-1/-2;at 0.45 MPa |
Heat Deflection temperature | 50 | ºC | ISO 75-1/-2;at 1.8 MPa |
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
Tensile modulus-MD | 600 | MPa | ISO 527-1/-2 |
Charpy Impact Strength (notched) | 110 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C;Partial break |
Yield Stress -MD | 30 | MPa | ISO 527-1/-2 |
Elongation at yield | 35 | % | ISO 527-1/-2 |
Strain at break-MD | >50 | % | ISO 527-1/-2 |
Chemical Properties | |||
Moisture absorption | 3.5 | % | Sim. to ISO 62 |
Water absorption | 1.0 | % | Sim. to ISO 62 |
Process Properties | |||
Drying Temperature | 80 | ºC |