Technical Documents
VESTAMID® LX9008 is a plasticizer-free polyamid 12 compound, with an especially high long-therm resistance under thermal load.
Details Compound
Product Type
Applications
Producer
Supplier
Advantages
- high long-therm resistance under thermal load
- absorbs only little moisture
- nearly unaffected dimensions
- properties of the finished parts at changing ambient conditions
Other Applications
to produce flexible tubes that are permanently exposed to higher temperatures, e.g., in the engine compartment of motor vehicles.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Shrinkage | 0.2 | % | ISO 294-4,2577; parallel |
Shrinkage | 1.9 | % | ISO 294-4,2577; normal |
Density | 1.01 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 45 | ºC | ISO 75-1/-2;at 1.8 MPa |
Heat Deflection temperature | 125 | ºC | ISO 75-1/-2;at 0.45 MPa |
Melting point | 176 | ºC | 10°C/min; ISO 11357-1/-3 |
Flameability | IEC 60695-11-10@Thickness 3.2 mm | ||
Vicat softening temperature | 145 | ºC | 50°C/hr/50 N; ISO 306 |
Dry Time | 480 - 960 | min | |
Flameability | IEC 60695-11-10@Thickness 1.60 mm | ||
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
Charpy Impact Strength (notched) | 45 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C;Partial break |
Tensile modulus-MD | 1450 | MPa | ISO 527-1/-2 |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
Yield Stress -MD | 42 | MPa | ISO 527-1/-2 |
Charpy Impact Strength (notched) | 22 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Elongation at yield | 5 | % | ISO 527-1/-2 |
Strain at break-MD | >50 | % | ISO 527-1/-2 |
Chemical Properties | |||
Moisture absorption | 0.7 | % | Sim. to ISO 62 |
Water absorption | 1.4 | % | Sim. to ISO 62 |
Electrical Properties | |||
Dissipation Factor | 0.032 | IEC 60250 @ 1 MHz | |
Dissipation Factor | 0.052 | IEC 60250 @100 Hz | |
Volume resistance | 1.00e+12 | ohm-cm | IEC 60093 |
Dielectric Strength | 37 | Kv/mm | IEC 60243-1 |
Relative permittivity | 3.7 | IEC 60250 @100 Hz | |
Relative permittivity | 2.9 | IEC 60250 @ 1 MHz | |
Process Properties | |||
Drying Temperature | 80 | ºC |