Technical Documents
VESTAMID® LX9012 has especially been developed for the extrusion and co-extrusion of ski upper and decorative films.
Details Compound
Product Type
Applications
Producer
Supplier
Advantages
- high transparency
- good screen and sublimation printing
- outstanding scratch resistance
- excellent impact strength at low temperature
- absorb only quantities of water
Other Applications
ski upper and decorative films
decoration on the bottom side of injection molded sports shoe soles
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.01 | g/ml | ISO 1183 |
Shrinkage | 1.0 | % | ISO 294-4,2577; parallel |
Shrinkage | 1.4 | % | ISO 294-4,2577; normal |
Thermal Properties | |||
Vicat softening temperature | 130 | ºC | 50°C/hr/50 N; ISO 306 |
Melting point | 176 | ºC | 10°C/min; ISO 11357-1/-3 |
Heat Deflection temperature | 45 | ºC | ISO 75-1/-2;at 1.8 MPa |
Heat Deflection temperature | 120 | ºC | ISO 75-1/-2;at 0.45 MPa |
Dry Time | 480 - 960 | min | |
Flameability | IEC 60695-11-10@Thickness 3.2 mm | ||
Flameability | IEC 60695-11-10@Thickness 1.60 mm | ||
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
Charpy Impact Strength (notched) | 19 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
Tensile modulus-MD | 1100 | MPa | ISO 527-1/-2 |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
Elongation at yield | 5 | % | ISO 527-1/-2 |
Yield Stress -MD | 37 | MPa | ISO 527-1/-2 |
Strain at break-MD | >50 | % | ISO 527-1/-2 |
Charpy Impact Strength (notched) | 15 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Chemical Properties | |||
Moisture absorption | 0.8 | % | Sim. to ISO 62 |
Water absorption | 1.5 | % | Sim. to ISO 62 |
Electrical Properties | |||
Volume resistance | 1.00e+12 | ohm-cm | IEC 60093 |
Dissipation Factor | 0.053 | IEC 60250 @100 Hz | |
Relative permittivity | 3.8 | IEC 60250 @100 Hz | |
Dissipation Factor | 0.028 | IEC 60250 @ 1 MHz | |
Dielectric Strength | 36 | Kv/mm | IEC 60243-1 |
Relative permittivity | 3.0 | IEC 60250 @ 1 MHz | |
Process Properties | |||
Drying Temperature | 80 | ºC | |
Mold Temperature | 80 | ºC | Injection molding |