myTechnical Documents
Medium viscosity, natural color polyamide 1010 basic polymer. It is semi-crystalline, which is the reason for its high mechanical resistance as well as chemical stability.
Details
Product Type
Applications
Producer
Supplier
Chemical Composition
the polycondensation product of 1,10-decamethylene diamine (D) and 1,10-decanedioic acid (sebacic acid—S)
Advantages
- high mechanical resistance
- chemical stability
- based on natural, renewable resources up to 100%
- high dimensional stability
- high strength
Other Applications
manufacture films with good transparency
Handling
It absorbs only little water.
As a result its mechanical properties vary little when exposed to changing environmental humidity.
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Appearance | Natural colors | ||
| Physical state | Granvl- cylindrical | ||
| Physical Properties | |||
| Density | 1.05 | g/ml | ISO 1183, 23°C |
| Melting range | 210 - 240 | ºC | |
| Thermal Properties | |||
| Vicat softening temperature | 196 | ºC | ISO 306, 10 N |
| Vicat softening temperature | 171 | ºC | ISO 306, 50 N |
| Dry Time | 120 - 240 | min | |
| Melting point | 200 | ºC | ISO 11357, 2nd heating, DSC |
| Mechanical Properties | |||
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU, -30°C | |
| viscosity number | 160 | ml/g | ISO 307 |
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU, 23°C | |
| Tensile modulus-MD | 1700 | MPa | ISO 527-1 |
| Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179/1eA, -30°C, Complete break, incl. hinge break H |
| Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179/1eA, 23°C, Complete break, incl. hinge break H |
| Strain at break-MD | >50 | % | ISO 527-1 |
| Tensile Stress at yield-TD | 54 | Mpa | ISO 527-2 |
| Strain at break-MD | >50 | % | ISO 527-2 |
| Tensile Stress at yield-TD | 54 | Mpa | ISO 527-1 |
| Tensile modulus-MD | 1700 | MPa | ISO 527-2 |
| Chemical Properties | |||
| Water absorption | 1.8 | % | ISO 62, at Saturation |
| Process Properties | |||
| Drying Temperature | 80 - 100 | ºC | |
| Mold Temperature | 60 - 100 | ºC | |