Technical Documents
Details Compound
Product Type
Reinforced with
Industry
Producer
Supplier
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.65 | g/ml | ISO 1183 |
MFI | 36.3 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
Linear Mold Shrinkage | 0.003 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
Linear Mold Shrinkage | 0.017 | cm/cm | Transverse |
Thermal Properties | |||
Heat Deflection temperature | 221 | ºC | at 0.46 MPa-ISO 75-1/-2 |
Flameability | IEC 60695@Thickness 1.60 mm | ||
Flameability | IEC 60695@Thickness 0.800 mm | ||
Mechanical Properties | |||
Tensile modulus-MD | 8000 | MPa | ISO 527-1/-2 |
Tensile Stress at break-MD | 100.0 | MPa | ISO 527-1/2 |
Elongation at break-MD | 1.7 | % | ISO 527-1/2 |
(Charpy Impact Strength(unnotched | 42 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 9 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched | 42 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
Charpy Impact Strength (notched) | 9 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Chemical Properties | |||
Water absorption | 0.40 | % | ISO 62 -at Saturation |
Electrical Properties | |||
Comparative Tracking Index | 175 | V | Test Solution A CTI; IEC 60112 |
Comparative Tracking Index | 150 | V | 100 drops value; IEC 60112 |
Surface Resistance | 1.00e+15 | ohm | IEC 60093 |
Dielectric Strength | 30.0 | Kv/mm | K20/P50; IEC 60243-1 |