myTechnical Documents
Details Compound
Product Type
Reinforced with
Industry
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.84 | g/ml | ISO 1183 |
| MFI | 18.4 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Linear Mold Shrinkage | 0.002 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Linear Mold Shrinkage | 0.010 | cm/cm | Transverse |
| Thermal Properties | |||
| Vicat softening temperature | 215 | ºC | Method A, 10 N; ISO 75-1/-2 |
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| Flameability | IEC 60695@Thickness 1.60 mm | ||
| Mechanical Properties | |||
| Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| (Charpy Impact Strength(unnotched | 50 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| Tensile Stress at break-MD | 130 | MPa | ISO 527-1/2 |
| Elongation at break-MD | 1.1 | % | ISO 527-1/2 |
| Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Tensile modulus-MD | 15000 | MPa | ISO 527-1/-2 |
| (Charpy Impact Strength(unnotched | 50 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Chemical Properties | |||
| Water absorption | 0.40 | % | ISO 62 -at Saturation |
| Electrical Properties | |||
| Surface Resistance | 1.00e+15 | ohm | IEC 60093 |
| Comparative Tracking Index | 250 | V | 100 drops value; IEC 60112 |
| Comparative Tracking Index | 275 | V | Test Solution A CTI; IEC 60112 |
| Dielectric Strength | 30.0 | Kv/mm | K20/P50; IEC 60243-1 |