myTechnical Documents
Details Compound
Product Type
Reinforced with
Industry
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| MFI | 50.4 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Density | 1.80 | g/ml | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Linear Mold Shrinkage | 0.016 - 0.018 | cm/cm | Transverse |
| Thermal Properties | |||
| Flameability | IEC 60695@Thickness 0.400 mm | ||
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| Heat Deflection temperature | 221 | ºC | at 0.46 MPa-ISO 75-1/-2 |
| Maximum Service Temperature | 310 | ºC | Short Term Heat Resistance after crosslinking (Soldering Tip) |
| Mechanical Properties | |||
| Tensile modulus-MD | 9300 | MPa | ISO 527-1/-2 |
| Tensile Stress at break-MD | 85.0 | MPa | ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Elongation at break-MD | 1.2 | % | ISO 527-1/2 |
| Charpy Impact Strength (notched) | 4 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Electrical Properties | |||
| Comparative Tracking Index | 175 | V | Test Solution A CTI; IEC 60112 |