myTechnical Documents
Details Compound
Product Type
Reinforced with
Industry
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.77 | g/ml | ISO 1183 |
| Linear Mold Shrinkage | 0.011 | cm/cm | Transverse |
| Linear Mold Shrinkage | 0.002 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Linear Mold Shrinkage | 0.0010 | cm/cm | Post Shrinkage (5 h, 140°C) on 2 mm |
| MFI | 49.56 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Linear Mold Shrinkage | 0.0030 | cm/cm | Post Shrinkage (5 h, 140°C) on 2 mm sheets with film gate at rim, mold temperature 80°C, Transverse |
| Thermal Properties | |||
| Flameability | IEC 60695@Thickness 1.60 mm | ||
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| Mechanical Properties | |||
| Tensile Stress at break-MD | 95.0 | MPa | ISO 527-1/2 |
| Elongation at break-MD | 1.2 | % | ISO 527-1/2 |
| Tensile modulus-MD | 10500 | MPa | ISO 527-1/-2 |
| (Charpy Impact Strength(unnotched | 30 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 5 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |