Technical Documents
Modified PBT resin with high flexibility, self-extinguishing, meets UL 94 with non-migrating flame retardant agent for injection molding and extruding.Applications: Cable insulation.
Details
Product Type
Applications
Producer
Supplier
Advantages
- high flexibility
- self-extinguishing
- flame retardant
Other Applications
Cable insulation
injection molding and extruding
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.38 | g/ml | |
MFI | 10 | g/10min | |
Thermal Properties | |||
Thermal Expansion | 100 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
Thermal Expansion | 100 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
Heat Deflection temperature | 95.0 | ºC | at 0.46 MPa |
Heat Deflection temperature | 40.0 | ºC | at 1.8 MPa |
Flameability | Thickness 1.60 mm@ | ||
Flameability | Thickness 3.20 mm@ | ||
Vicat softening temperature | 125 | ºC | 50°C/hr/50 N |
Mechanical Properties | |||
Creep modulus | 650 | MPa | 1000hours |
Creep modulus | 950 | MPa | 1hour |
Tensile Impact strength | 100 | Kj/m² | |
Tensile modulus-MD | 1000 | MPa | |
Elongation at break-MD | >50 | % | |
(Charpy Impact Strength(unnotched | kJ/m² | ||
Charpy Impact Strength (notched) | 7 | kJ/m² | |
(Charpy Impact Strength(unnotched | 90 | kJ/m² | Temperature -30.0 °C@ |
Charpy Impact Strength (notched) | 3 | kJ/m² | Temperature -30.0 °C@ |
Tensile Stress at yield-MD | 33.0 | MPa | |
Elongation at yield | 15 | % | |
Chemical Properties | |||
Moisture absorption | <0.50 | % | at Equilibrium |
Water absorption | 0.00 | % | |
Electrical Properties | |||
Electrical Resistivity | >1.00e+15 | ohm-cm | |
Dielectric Constant | 4.0 | Frequency 1e+6 Hz@ | |
Surface Resistance | 1.00e+14 | ohm | |
Dielectric Strength | 25.0 | Kv/mm | |
Dissipation Factor | 0.015 | Frequency 100 Hz@ | |
Dielectric Constant | 3.0 | Frequency 100 Hz@ | |
Dissipation Factor | 0.025 | Frequency 1e+6 Hz@ | |
Comparative Tracking Index | 200 | V |