Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.42 | g/ml | |
MFI | 13 | g/10min | |
Thermal Properties | |||
UL RTI | 140 | ºC | Mechanical without Impact |
UL RTI | 130 | ºC | Mechanical with Impact |
UL RTI | 130 | ºC | Electrical |
Flameability | @Thickness 3.20 mm | ||
Flameability | @Thickness 1.60 mm | ||
Thermal Expansion | 100 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
Vicat softening temperature | 155 | ºC | 50°C/hr/50 N |
Heat Deflection temperature | 55.0 | ºC | at 1.8 MPa |
Heat Deflection temperature | 150 | ºC | at 0.46 MPa |
Thermal Expansion | 100 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
Mechanical Properties | |||
Creep modulus | 1100 | MPa | 1000hours |
Charpy Impact Strength (notched) | 3 | kJ/m² | |
Charpy Impact Strength (notched) | 3 | kJ/m² | @Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 65 | kJ/m² | @Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 90 | kJ/m² | |
Tensile modulus-MD | 2200 | MPa | |
Elongation at break-MD | >50 | % | |
Tensile Stress at yield-MD | 55.0 | MPa | |
Elongation at yield | 7.0 | % | |
Tensile Impact strength | 50.0 | Kj/m² | |
Creep modulus | 2200 | MPa | 1hour |
Chemical Properties | |||
Moisture absorption | <0.50 | % | Humidity Absorption-at Equilibrium |
Water absorption | 0.000 | % | |
Electrical Properties | |||
Dissipation Factor | 0.0060 | @Frequency 100 Hz | |
Dielectric Strength | 27.0 | Kv/mm | |
Dielectric Constant | 3.0 | @Frequency 100 Hz | |
Dielectric Constant | 3.0 | @Frequency 1e+6 Hz | |
Surface Resistance | 1.00e+14 | ohm | |
Electrical Resistivity | >1.00e+15 | ohm-cm | |
Dissipation Factor | 0.020 | @Frequency 1e+6 Hz | |
Comparative Tracking Index | 175 | V |