myTechnical Documents
Details Compound
Product Type
Reinforced with
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| MFI | 20.4 | g/10min | ISO 1133@Load 2.16 kg, Temperature 250 °C |
| Linear Mold Shrinkage | 0.013 | cm/cm | Transverse |
| Linear Mold Shrinkage | 0.0015 | cm/cm | sheet with film gate at rim, mold temperature 80°C @Thickness 2.00 mm |
| Density | 1.70 | g/ml | ISO 1183 |
| Thermal Properties | |||
| Heat Deflection temperature | 223 | ºC | ISO 75-1/-2;at 0.46 MPa |
| Flameability | IEC 60695@Thickness 1.60 mm | ||
| Heat Deflection temperature | 210 | ºC | ISO 75-1/-2;at 1.8 MPa |
| Vicat softening temperature | 210 | ºC | Method B, 50 N; ISO 306 |
| Vicat softening temperature | 220 | ºC | Method A, 10 N; ISO 306 |
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| Mechanical Properties | |||
| Charpy Impact Strength (notched) | 13 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 13 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| (Charpy Impact Strength(unnotched | 50 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| (Charpy Impact Strength(unnotched | 50 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Tensile Stress at break-MD | 180 | MPa | ISO 527-1/2 |
| Tensile modulus-MD | 14500 | MPa | ISO 527-1/-2 |
| Elongation at break-MD | 1.8 | % | ISO 527-1/2 |
| Chemical Properties | |||
| Water absorption | 0.40 | % | ISO 62;at Saturation |