Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.58 | g/ml | |
MFI | 8 | g/10min | |
Thermal Properties | |||
Vicat softening temperature | 210 | ºC | 50°C/hr/50 N |
Heat Deflection temperature | 210 | ºC | at 1.8 MPa |
Heat Deflection temperature | 223 | ºC | at 0.46 MPa |
Thermal Expansion | <50.0 | µm/m-°C | @Temperature 20.0 °C |
Flameability | @Thickness 1.60 mm | ||
Mechanical Properties | |||
Charpy Impact Strength (notched) | 14 | kJ/m² | @Temperature -30.0 °C |
Charpy Impact Strength (notched) | 20 | kJ/m² | |
(Charpy Impact Strength(unnotched | 75 | kJ/m² | @Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 80 | kJ/m² | |
Tensile modulus-MD | 9000 | MPa | |
Elongation at break-MD | 4.0 | % | |
Tensile strength | 110 | MPa | |
Chemical Properties | |||
Water absorption | 0.00 | % | |
Electrical Properties | |||
Dielectric Constant | 4.0 | @Frequency 100 Hz | |
Dielectric Constant | 3.0 | @Frequency 1e+6 Hz | |
Surface Resistance | 1.00e+13 | ohm | |
Electrical Resistivity | 1.00e+15 | ohm-cm | |
Dielectric Strength | 30.0 | Kv/mm | |
Dissipation Factor | 0.0075 | @Frequency 100 Hz | |
Dissipation Factor | 0.022 | @Frequency 1e+6 Hz | |
Comparative Tracking Index | 450 | V |