Description: VESTODUR X9406 is an impact modified compound based on polybutylene terephthalate. The resin is used as a barrier layer resin in multilayer tubing 1000.1 (MLT 1000.1)developed by Degussa.
Details
Product Type
Applications
Producer
Supplier
Advantages
- resistance against hydrocarbon permeation when alcohol containing fuels are used
- provides excellent barrier properties also in contact with fuels at elevated temperatures
Other Applications
barrier layer resin in multilayer tubing 1000.1 (MLT 1000.1)
Handling
MLT 1000.1 is a 3-layer-tubing comprising an outermost layer of VESTAMID LX9010, an adhesive layer of VESTODUR X9407, and an innermost layer of VESTODUR X9406.
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
MFI | 19.68 | g/10min | |
MFI | 73.8 | g/10min | ISO 1133, Temperature 260 °C |
MFI | 19.68 | g/10min | ISO 1133, Temperature 250 °C |
MFI | 8.61 | g/10min | |
MFI | 8.61 | g/10min | |
Density | 1.23 | g/ml | ISO 1183 |
MFI | 73.8 | g/10min | |
Thermal Properties | |||
Vicat softening temperature | 215 | ºC | Method A, 10 N; ISO 306 |
Heat Deflection temperature | 50.0 | ºC | ISO 75-1/-2;at 1.8 MPa |
Vicat softening temperature | 145 | ºC | Method B, 50 N; ISO 306 |
Heat Deflection temperature | 145 | ºC | ISO 75-1/-2;at 0.46 MPa |
Thermal Expansion | 140 | µm/m-°C | Longitudinal; ISO 11359, DIN 53752 @Temperature 23.0 - 80.0 °C |
Thermal Expansion | 140 | µm/m-°C | ; ISO 11359, DIN 53752 @Temperature 23.0 - 80.0 °C ;Transverse to Flow |
Mechanical Properties | |||
Elongation at yield | 3.8 | % | ISO 527-1/2 |
Hardness Shore D | 70 | ISO 868 | |
Charpy Impact Strength (notched) | 15 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
Elongation at break-MD | 40 | % | ISO 527-1/2 |
Tensile modulus-MD | 1750 | MPa | ISO 527-1/-2 |
Tensile Stress at yield-MD | 40.0 | MPa | ISO 527-1/2 |
Chemical Properties | |||
Water absorption | 0.60 | % | ISO 62; at Saturation |