Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Linear Mold Shrinkage | 0.020 | cm/cm | Transverse-Pigmentation can change mold shrinkage |
Linear Mold Shrinkage | 0.020 | cm/cm | Pigmentation can change mold shrinkage |
Melting range | 221 - 226 | ºC | DSC |
Density | 1.21 | g/ml | ISO 1183 |
MFI | 18.15 | g/10min | |
MFI | 18.15 | g/10min | |
Thermal Properties | |||
Vicat softening temperature | 125 | ºC | 50N; ISO 306 |
Vicat softening temperature | 215 | ºC | 10N; ISO 306 |
Flameability | @Thickness 1.60 mm | ||
Thermal Expansion | 150 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0-55.0 °C |
Thermal Expansion | 150 | µm/m-°C | Transverse to Flow; ISO 11359@Temperature 23.0-55.0 °C |
Flameability | @Thickness 0.800 mm | ||
Mechanical Properties | |||
Hardness Shore D | 65 | ISO 868 | |
Tensile modulus-MD | 1700 | MPa | ISO 527-1/2 |
Tensile Stress at yield-MD | 40.0 | MPa | 50mm/min; ISO 527-1/2 |
Elongation at break-MD | >50 | % | 50mm/min; ISO 527-1/2 |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
Charpy Impact Strength (notched) | 90 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C;Partial Break |
Charpy Impact Strength (notched) | 20 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Elongation at yield | 4.0 | % | 50mm/min; ISO 527-1/2 |
Chemical Properties | |||
Electrolytic Corrosion | IEC 60426 | ||
Electrical Properties | |||
Dielectric Constant | 3.0 | IEC 60250@Frequency 100 Hz | |
Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
Comparative Tracking Index | >600 | V | Test Solution A, CTI; IEC 60112 |
Comparative Tracking Index | 575 | V | Test Solution A, 100 drops; IEC 60112 |
Dissipation Factor | 0.0020 | IEC 60250@Frequency 100 Hz |