myTechnical Documents
Details Compound
Product Type
Applications
Industry
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.06 | g/ml | |
| MFI | 17 | g/10min | |
| Thermal Properties | |||
| Vicat softening temperature | 86 | ºC | 50°C/hr/50 N |
| Flameability | V-2@Thickness 3.20 mm | ||
| Flameability | V-2@Thickness 1.60 mm | ||
| Heat Deflection temperature | 82 | ºC | at 0.46 MPa |
| Thermal Expansion | <50 | µm/m-°C | @Temperature 20.0 °C |
| Heat Deflection temperature | 77 | ºC | at 1.8 MPa |
| Mechanical Properties | |||
| (Charpy Impact Strength(unnotched | 50 | kJ/m² | |
| Tensile modulus-MD | 2750 | MPa | |
| Elongation at break-MD | 30 | % | |
| Tensile Stress at yield-MD | 34 | MPa | |
| Elongation at yield | 1 | % | |
| (Charpy Impact Strength(unnotched | 40 | kJ/m² | @Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 4 | kJ/m² | |
| Chemical Properties | |||
| Moisture absorption | 0.0 | % | |
| Oxirane Oxygen Content | 26 | % | |
| Electrical Properties | |||
| Dissipation Factor | 0.00060 | @Frequency 100 Hz | |
| Dissipation Factor | 0.00060 | @Frequency 1e+6 Hz | |
| Surface Resistance | 1.00e+14 | ohm | |
| Dielectric Strength | 35 | Kv/mm | |
| Electrical Resistivity | >1.00e+15 | ohm-cm | |
| Dielectric Constant | 2 | @Frequency 100 Hz | |
| Dielectric Constant | 2 | @Frequency 1e+6 Hz | |
| Comparative Tracking Index | 300 | V | |