myTechnical Documents
Details Compound
Product Type
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.03 | g/ml | |
| MFI | 10 | g/10min | |
| Thermal Properties | |||
| Flameability | HB@Thickness 3.20 mm | ||
| Flameability | HB@Thickness 1.60 mm | ||
| Heat Deflection temperature | 79 | ºC | at 0.46 MPa |
| Thermal Expansion | <50 | µm/m-°C | @Temperature 20.0 °C |
| Vicat softening temperature | 83 | ºC | 50°C/hr/50 N |
| Heat Deflection temperature | 70 | ºC | at 1.8 MPa |
| Mechanical Properties | |||
| Tensile modulus-MD | 1750 | MPa | |
| (Charpy Impact Strength(unnotched | 160 | kJ/m² | |
| Elongation at break-MD | 50 | % | |
| Tensile Stress at yield-MD | 23 | MPa | |
| Elongation at yield | 1 | % | |
| (Charpy Impact Strength(unnotched | 110 | kJ/m² | @Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 10 | kJ/m² | |
| Chemical Properties | |||
| Oxirane Oxygen Content | 18 | % | |
| Moisture absorption | 0.0 | % | |
| Electrical Properties | |||
| Dielectric Strength | 58 | Kv/mm | |
| Surface Resistance | 1.00e+14 | ohm | |
| Electrical Resistivity | >1.00e+15 | ohm-cm | |
| Dielectric Constant | 2 | @Frequency 100 Hz | |
| Dielectric Constant | 2 | @Frequency 1e+6 Hz | |
| Comparative Tracking Index | 500 | V | |
| Dissipation Factor | 0.00030 | @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.00030 | @Frequency 100 Hz | |