XR407D ABS

Technical Documents

An acrylonitrile butadiene styrene (ABS) grade. It is suitable for processing through injection molding.

Details

CAS

25120-20-1, 9003-56-9, 25747-74-7, ;31621-07-5

Product Type

Polymer > ABS

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Lg Chem

Other Applications

Electric & Electronic Housing

Technical data

Quantity Value Unit Comment
dry Time 3 - 4 hr
Physical Properties
Melting range 230 - 250 ºC
Humidity <0.01 %
MFI 6 g/10min ASTM D1238;220℃/10kg
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm ASTM D955;(Flow), 3.2mm
Specific Gravity 1.07 ASTM D792
Thermal Properties
Flameability UL94;Thickness >=1.50 mm
Flameability UL94;Thickness >=3.00 mm
UL RTI 60 ºC UL 746B;Thickness >=3.00 mm;Mechanical without Impact
UL RTI 60 ºC UL 746B;Thickness >=1.50 mm;Mechanical without Impact
UL RTI 60 ºC UL 746B;Thickness >=1.50 mm;Mechanical with Impact
UL RTI 60 ºC UL 746B;Thickness >=3.00 mm;Mechanical with Impact
UL RTI 60 ºC UL 746B;Thickness >=3.00 mm;Electrical
UL RTI 60 ºC UL 746B;Thickness >=1.50 mm;Electrical
Vicat softening temperature 111 ºC ASTM D1525;5kg, 50℃/h
Heat Deflection temperature 104 ºC Unannealed; ASTM D648;Thickness 6.40 mm;at 1.8 MPa
Heat Deflection temperature 113 ºC Unannealed; ASTM D648;Thickness 6.40 mm;at 0.46 MPa
Mechanical Properties
Izod impact strength (unnotched) 78.5 J/m ASTM D256;-30℃;3.2mm
Izod impact strength (unnotched) 78.5 J/m ASTM D256;-30℃;6.4mm
Izod impact strength (notched) 167 J/m ASTM D256;23℃;3.2mm
Izod impact strength (notched) 157 J/m ASTM D256;23℃;6.4mm
Flexural modulus-MD 2450 MPa ASTM D790;15mm/min;3.2mm
Flexural strength 77.5 MPa ASTM D790;15mm/min;3.2mm;Yield
Elongation at break-MD 20 % ASTM D638;50mm/min;3.2mm
Tensile Stress at yield-MD 47.1 MPa ASTM D638;50mm/min;3.2mm
Rockwell Hardness 111 ASTM D785;Rockwell R
Process Properties
Middle Barrel Temperature 220 - 240 ºC
Mold Temperature 60 - 80 ºC
Drying Temperature 80 - 90 ºC