myTechnical Documents
Acrylic-Based Multipolymer Molding Compound.
Details Compound
Product Type
Producer
Supplier
Advantages
- clarity
- gloss
- toughness
- resistance to fatty acids
Other Applications
molding applications
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Refractive index | 1.515 | ASTM D542 | |
| Physical Properties | |||
| Melting range | 216 - 249 | ºC | |
| Density | 1.12 | g/ml | ASTM D792 |
| MFI | 4.0 | g/10min | ASTM D1238@Load 5.00 kg, Temperature 230 °C |
| Viscosity | 2.00e+6 | cP | Approximate value@Shear Rate 100 1/s, Temperature 240 °C |
| Thermal Properties | |||
| Specific Heat Capacity | 1.30 | J/gºC | @Temperature 25.0 °C |
| Heat Deflection temperature | 83.0 | ºC | ASTM D648;at 1.8 MPa |
| Vicat softening temperature | 94.0 | ºC | ASTM D1525 |
| Specific Heat Capacity | 1.90 | J/gºC | @Temperature 100 °C |
| Specific Heat Capacity | 2.30 | J/gºC | @Temperature 175 °C |
| Thermal Conductivity | 0.220 | W/mk | |
| Flow | 740 | mm | Spiral Flow; 215°C; 1/4 in half round channel |
| Mechanical Properties | |||
| Elongation at yield | 3.0 | % | ASTM D638 |
| Tensile strength | 61.0 | MPa | ASTM D638;ultimate |
| Izod impact strength (notched) | 43.0 | J/m | bar; ASTM D256@Diameter 6.35 mm |
| Rockwell Hardness | 60 | ASTM D785;Rockwell M | |
| Tensile modulus-MD | 3400 | MPa | ASTM D638 |
| Elongation at break-MD | 11 | % | ASTM D638 |
| Flexural strength | 90.0 | MPa | ASTM D790; at Yield |
| Flexural modulus-MD | 2800 | MPa | ASTM D790 |
| Chemical Properties | |||
| Oxirane Oxygen Content | 17.2 | % | ASTM D2863 |
| Optical Properties | |||
| Haze | 4.0 | % | ASTM D1003 |
| Transmittance | 84 | % | ASTM D1003;visible |