myTechnical Documents
Acrylic-Based Multipolymer Molding Compound.
Details Compound
Product Type
Producer
Supplier
Other Applications
molded parts
refrigerator parts
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Refractive index | 1.515 | ASTM D542 | |
| Physical Properties | |||
| Bulk density | 0.650 | g/ml | Apparent Bulk Density; ASTM D1895 |
| MFI | 4.0 | g/10min | ASTM D1238@Load 5.00 kg, Temperature 230 °C |
| Density | 1.11 | g/ml | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 | cm/cm | ASTM D551 |
| Thermal Properties | |||
| Vicat softening temperature | 101 | ºC | ASTM D1525 |
| Heat Deflection temperature | 90.0 | ºC | Annealed;ASTM D648;at 1.8 MPa |
| Thermal Expansion | 79.0 | µm/m-°C | ;;linear@Temperature 0.000-100.0 °C |
| Specific Heat Capacity | 1.90 | J/gºC | @Temperature 100 °C |
| Thermal Conductivity | 0.220 | W/mk | |
| Specific Heat Capacity | 2.30 | J/gºC | @Temperature 175 °C |
| Specific Heat Capacity | 1.30 | J/gºC | @Temperature 25.0 °C |
| Flameability | |||
| Mechanical Properties | |||
| Charpy Impact Strength (notched) | 9.10 | kJ/m² | J/cm; ASTM D256 |
| Compressive Strength | 79.0 | MPa | ASTM D695; at Yield |
| Flexural modulus-MD | 2700 | MPa | ASTM D790 |
| Elongation at break-MD | 5.6 | % | ASTM D638 |
| Flexural strength | 87.0 | MPa | ASTM D790; at Yield |
| Tensile modulus-MD | 2800 | MPa | ASTM D638 |
| Rockwell Hardness | 48 | ASTM D785;Rockwell M | |
| Izod impact strength (notched) | 64.0 | J/m | bar; ASTM D256@Diameter 6.35 mm |
| Tensile strength | 57.0 | MPa | ASTM D638;ultimate |
| Elongation at yield | 3.0 | % | ASTM D638 |
| Izod impact strength (notched) | 48.0 | J/m | bar; ASTM D256@Diameter 6.35 mm,Temperature 0.000 °C |
| Chemical Properties | |||
| Water absorption | <0.30 | % | ASTM D570 |
| Optical Properties | |||
| Transmittance | 88 | % | ASTM D1003;visible |
| Haze | 7.0 | % | ASTM D1003 |